Product Description
Ultra C6 is inherently protective, which allows for the ultimate in protection against extreme radiant and intense heat without the risk of the protective nature being "washed out." Ultra C6 fabrics are lightweight, offer excellent moisture wicking, greater water vapor transfer, and breathability.
MATERIAL SPECIFICATIONS
INTERLOCK C6 BLACK PREMIUM WEIGHT
| Material Content: | 65% Oxidized Polyacrylonitrile (OPF)/35% artificial tri-blend |
| Material Construction: | Interlock Knit |
| Material Weight: |
8.5 oz / yd2(+1 / -.5) |
| Material Color: | Black (Standard) |
| Color Options Available: |
FABRIC PERFORMANCE VALUES
4th generation advanced CARBON technology
3 elements needed for fire=Oxygen, Heat, and Fuel
Without one element, a fire cannot start or continue
When exposed to flame, C6 fibers expand,
creating an Oxygen starved environment
so fire cannot continue. Material is self extinguishing
Inherently flame resistant (no harsh chemical treatments)
Odor neutralizing, Anti-Static, Low Heat Conductivity
Maintains performance values after laundering
Finished to minimize shrinkage
Interlock knit allows for stretch and shape retention
Interlock knit for smooth, sleek, protective surface
Majestic Fire Apparel is a vertical manufacturer
Knitting our own fire retardant materials for over 17 years.
We knit, cut, sew, and ship-all from our location in PA.
MADE IN USA
NFPA 70E PERFORMANCE SPECIFICATIONS OF
ASTM F 1959/F 1959M-06ae1:
HRC Level 1 = minimum 5 cal/cm2 to 7 cal/cm2
HRC Level 2 = minimum 8 cal/cm2 to 24 cal/cm2
HRC Level 3 = minimum 25 cal/cm2 to 39 cal/cm2
HRC Level 4 = minimum 40 cal/cm2 and over
Meets CAL-OSHA Requirements
Passes Federal Test 191, Method 5903.2; CAL OSHA Sections 3406(d)
Complies with OSHA Rule 29 CFR Part 1910, 269
Fabric Performance Values in accordance with NFPA 1971-2013 test report dated 3/15/2013 performed by Underwriters Laboratories
ATPV and HAF values found in accordance with ASTM International Standard Test Method F1959-1999. Tests performed by Hugh Hoagland
all weights and measurements are approximate
| THERMAL PROTECTIVE PERFORMANCE (TPP) | ||
| as received | ||
| after 5 washes | ||
| HOOD MATERIAL BURST STRENGTH | ||
| FLAME RESISTANCE TEST | ||
| After Flame | as received | |
| after 5 washes | ||
| Char Length (wales x courses) | as received | |
| after 5 washes | ||
| CLEANING SHRINKAGE RESISTANCE TEST | ||
| Hood Measurement | ||
| Face Opening Measurement | ||
| HEAT AND THERMAL SHRINKAGE RESISTANCE TEST | ||
| Hood Measurement | as received | |
| after 5 washes | ||
| Face Opening Measurement | as received | |
| after 5 washes | ||
| SEAM BREAKING STRENGTH TEST | ||
| MELT, DRIP, IGNITE, SEPARATE WHEN EXPOSED TO FLAME | ||
| ARC THERMAL PERFORMANCE VALUE (ATPV) | ||
| 1 ply | 21.2cal/cm2 | |
| 2 ply | 52.7 cal/cm2 | |
| 3 ply | 58.6 cal/cm2 | |
| HEAT ATTENUATION FACTOR (HAF) | ||
| 1 ply | 88% | |
| 2 ply | 93% | |
| 3 ply | ||
| MOLTEN METAL SPLASH PROTECTION TEST | ||
| Time to 2nd degree burn according to Stoll Curve | 1 ply as received | 2.2 |
| 1 ply after laundering | NONE | |
| |
||
4th generation advanced CARBON technology
3 elements needed for fire=Oxygen, Heat, and Fuel
Without one element, a fire cannot start or continue
When exposed to flame, C6 fibers expand,
creating an Oxygen starved environment
so fire cannot continue. Material is self extinguishing
Inherently flame resistant (no harsh chemical treatments)
Odor neutralizing, Anti-Static, Low Heat Conductivity
Maintains performance values after laundering
Finished to minimize shrinkage
Interlock knit allows for stretch and shape retention
Interlock knit for smooth, sleek, protective surface
Majestic Fire Apparel is a vertical manufacturer
Knitting our own fire retardant materials for over 17 years.
We knit, cut, sew, and ship-all from our location in PA.
MADE IN USA
NFPA 70E PERFORMANCE SPECIFICATIONS OF
ASTM F 1959/F 1959M-06ae1:
HRC Level 1 = minimum 5 cal/cm2 to 7 cal/cm2
HRC Level 2 = minimum 8 cal/cm2 to 24 cal/cm2
HRC Level 3 = minimum 25 cal/cm2 to 39 cal/cm2
HRC Level 4 = minimum 40 cal/cm2 and over
Meets CAL-OSHA Requirements
Passes Federal Test 191, Method 5903.2; CAL OSHA Sections 3406(d)
Complies with OSHA Rule 29 CFR Part 1910, 269
Fabric Performance Values in accordance with NFPA 1971-2013 test report dated 3/15/2013 performed by Underwriters Laboratories
ATPV and HAF values found in accordance with ASTM International Standard Test Method F1959-1999. Tests performed by Hugh Hoagland